Commercial calcium silicate bearing Portland cement type III (PC III), in the form of agglomerated cement sorbent (ACS) pellets, is being investigated for in-situ desulfurization of fuel gases and for improved coal gasification. The preparation procedure and conditions for pelletizing agglomerated cement sorbent (ACS) by a low energy, low cost agglomeration technique have been modified using a two-stage pelletization procedure, which yields ACS pellets of greater mechanical strength. A 40 mm ID bench scale fluidized bed gasifier (FBG) was used to determine sulfur removal efficiency of ACS pellets as well as their attrition resistance, using a simulated gas mixture. These tests show that 90% or more of the sulfur removal from the gas is achieved until 35% of the ACS pellet is sulfidated and that it has excellent attrition resistance (less than 0.1% wt loss) during cyclic tests excluding the first conditioning cycle. The gasification of coal by partial oxidation with air to low Btu gas was conducted in a 1-inch bench scale FBG unit by our collaborator, the Foster Wheeler Corporation (FWC). At temperatures between 800/sup 0/C and 950/sup 0/C the efficiency of coal gasification is improved by as much as 40% when ACS pellets are used compared to the use of Greer limestone. At the same time the sulfur removal efficiency is increased from 50 to 65% with Greer limestone to over 95% with the ACS pellets. The test on sulfur fixation characteristics of the sorbent in the 1-inch FBG unit using a simulated gas also shows that the ACS pellet is much more reactive toward H/sub 2/S than Greer limestone. The ability of ACS pellets to simultaneously desulfurize and improve the gasification efficiency of coal in FBG justifies further investigation.