Corrosion and erosion/corrosion testing of gas turbine materials in the effluent from a pressurized fluidized bed coal combustor continues under the Long Term Materials Test program. Two 1000-hour erosion/corrosion screening tests of twelve candidate gas turbine vane and blade base alloys and a variety of protective coating systems have been completed. Test conditions included 1350/sup 0/F, 800 to 900 ft/s and particulate loadings of 30 to 90 ppM. Erosion/corrosion degradation rates of 1 to 4 mils/1000 hours were observed with corrosion predominant in areas of particle impaction. FeCrAlY, CoCrAlY and rhodium aluminide coatings show significantly better resistance to degradation than unprotected base alloys, aluminide or platinum-aluminide diffusion coatings.